  • No Thumbnail Available
    Item
    Comparison of Fracture Resistance of Endodontically Treated Teeth Restored with FiberSite Postsystem and Glass Fiber, Combined with Different Root Canal Sealers
    (2021) Eren, Birgul; Ozasir, Tufan; Kandemir, Baris; Gulsahi, Kamran; https://orcid.org/0000-0001-6424-2250; https://orcid.org/0000-0001-8778-9005; https://orcid.org/0000-0003-3510-7265; 34725637
    This study is aimed at evaluating the effects of FiberSite and glass fiber postsystems on the fracture resistance of endodontically restored teeth, when combined with various root canal sealers. Forty human mandibular premolar teeth, each having a single root with anatomically comparable dimension and length, were selected. The teeth in each experimental group (n = 10) were instrumented, obturated, and restored with the following procedures: in group 1, AH Plus root canal sealer and a glass fiber post with a composite core; in group 2, AH Plus root canal sealer and a FiberSite postsystem; in group 3, Sure-Seal Root canal sealer and a glass fiber post with a composite core; and in group 4, Sure-Seal Root canal sealer and a FiberSite postsystem. The specimens were placed on a universal test machine. The fracture resistance of all specimens was tested using generic test equipment, and the value of the force in newton (N) during fracture was measured for each root. A statistical analysis was conducted through the Kruskal-Wallis test as well as the post hoc test. The tests showed a significant difference between groups 2 and 3, with group 3 producing load values that were significantly higher than group 2. In contrast, no significant differences were found to exist between the other groups. Regardless of postsystems, groups 3 and 4 showed higher mean fracture values (but no statistically significant differences) than groups 1 and 2.
  • No Thumbnail Available
    Item
    The Effect of Radiotherapy on the Marginal Adaptation of Class II Direct Resin Composite Restorations: A Micro-computed Tomography Analysis
    (2022) Oglakci, B.; Burduroglu, D.; Eris, A. H.; Mayadagli, A.; Arhun, N.; 35226728
    This laboratory study was designed to evaluate the marginal adaptation of Class II mesio-occluso-distal (MOD) restorations at the cervical region with micro-computed tomography (micro-CT). Two groups of restorations were compared: 1) those that had been exposed to radiotherapy before restoration was performed using a universal adhesive in etch-and-rinse and self-etch modes; and 2) those that had previously been restored using a universal adhesive in etch-and-rinse and self-etch modes and had subsequently undergone radiotherapy. Sixty intact human molars were randomly divided into groups according to irradiation status: no radiotherapy (control group); radiotherapy followed by restoration (radiotherapy-first group); and restoration followed by radiotherapy (restoration-first group). These three groups were then subdivided into two groups each on the basis of adhesive application type (etch-and-rinse and self-etch modes), for a total of six groups (n=10/group). Standardized Class II MOD cavities were prepared. A universal adhesive (Clearfil Universal Bond Quick, Kuraray, Okayama, Japan) was applied. The teeth were restored with resin composite (Estelite Posterior Quick, Tokuyama, Tokyo, Japan). The radiotherapy protocol was conducted with 60 gray (Gy) at 2 Gy/day, five days a week for six weeks. Adhesive defects were analyzed in distal and mesial views and evaluated with micro-CT (SkyScan 1174v2, Kontich, Antwerp, Belgium) on the basis of the volume of black spaces between the cavity walls and the restorative materials (mm(3)). The data were analyzed using the Kruskal-Wallis, Mann Whitney U and Wilcoxon tests (p<0.05). The radiotherapy protocol did not affect the marginal adaptation of the universal adhesive at the cervical regions. Regarding the application modes, for the radiotherapy-first group, the self-etch mode caused significantly higher adhesive defects than the etch-and-rinse mode at the dentin margin. For the no-radiotherapy group, the adhesive defects at the dentin margin were significantly higher than at the enamel margin with the application of the etch-and-rinse mode.